The aim of this book is to measure the flow characteristics of blast furnace slag. The industrial slag, synthetically prepared in the laboratory by pure oxides as obtained from market and iron bearing materials with various extents of reduction resembling that expected to be in the cohesive zone as per literature are chosen for measurement while the final slag obtained from the industry reveals shortness of the slag. At C/S ratio of 1.04 to 1.09 and 10.4 to 11.01 MgO % the synthetic slag does not shown a clear trained, the iron bearing materials reveals variation of the characteristics temperature with variation in the extend of the reduction, SEM micrograph and XRD plots of the iron bearing material with different extended of reduction reveal compositional changes associated with structural changes.
Die bei uns gelisteten Preise basieren auf Angaben der gelisteten Händler zum Zeitpunkt unserer Datenabfrage. Diese erfolgt einmal täglich. Von diesem Zeitpunkt bis jetzt können sich die Preise bei den einzelnen Händlern jedoch geändert haben. Bitte prüfen sie auf der Zielseite die endgültigen Preise.
Die Sortierung auf unserer Seite erfolgt nach dem besten Preis oder nach bester Relevanz für Suchbegriffe (je nach Auswahl).
Für manche Artikel bekommen wir beim Kauf über die verlinkte Seite eine Provision gezahlt. Ob es eine Provision gibt und wie hoch diese ausfällt, hat keinen Einfluß auf die Suchergebnisse oder deren Sortierung.
Unser Preisvergleich listet nicht alle Onlineshops. Möglicherweise gibt es auf anderen bei uns nicht gelisteten Shops günstigere Preise oder eine andere Auswahl an Angeboten.
Versandkosten sind in den angezeigten Preisen und der Sortierung nicht inkludiert.
* - Angaben ohne Gewähr. Preise und Versandkosten können sich zwischenzeitlich geändert haben. Bitte prüfen sie vor dem Kauf auf der jeweiligen Seite, ob die Preise sowie Versandkosten noch aktuell sind.